Titel: Analysis of the Weld Seam Area of Magnetic Pulse Welded Aluminium-Steel-Sheet-Connections on its Suitability as a Sign of Quality
Sprache (ISO): en
Zusammenfassung: This paper deals with the characterisation of the weld seam area of magnetic pulse welded aluminium-steel-sheet-connections for different material combinations and its suitability as a sign of quality. The goal of this work is to suggest a relationship between the weld seam area and the strength of the generated joint. Based on the results of this work, the weld seam area could be established as a basis of design and for dimensioning the magnetic pulse welded hybrid joints. To identify the correlation of the generated weld seam area with the maximum tensile force of the welded samples, several aluminium-steel-joints were welded and tested using tensile shear test. Thereafter, the weld seam area was measured and correlated to the maximum bearable tensile force of the joint. The tested material combinations were EN AW-1050A-H14 / S235JR and EN AW-6016-T6 / HCT780X. The results illustrate a positive linear correlation between the weld seam area of the joint and the maximum tensile force. At the same time further weld seam irregularities were identified which have to be considered for evaluating the suitability of the weld seam area as a sign of quality. Additionally, in order to prevent such irregularities or to ensure a good weld seam, the non-destructive testing method of active thermography is presented.
Schlagwörter: magnetic pulse welding
aluminium
steel
Schlagwörter (RSWK): Aluminium
Stahl
URI: http://hdl.handle.net/2003/36974
http://dx.doi.org/10.17877/DE290R-18973
Erscheinungsdatum: 2018-05-15
Ist Teil von: 8th International Conference on High Speed Forming
Enthalten in den Sammlungen:ICHSF 2018

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
ICHSF2018-Paper_Schumacher.pdfDNB604.74 kBAdobe PDFÖffnen/Anzeigen


Diese Ressource ist urheberrechtlich geschützt.



Diese Ressource ist urheberrechtlich geschützt. rightsstatements.org