Authors: Biermann, Oliver
Title: Molecular dynamics simulation study of polyelectrolyte adsorption on cellulose surfaces
Language (ISO): en
Abstract: The adsorption of two polyelectrolyte ((carboxy methyl) cellulose and poly(acrylate) in water on crystalline cellulose is studied in this work. The multi-component problem has been splitted up into simulations of solutions of the polyelectrolyte (polyanions including sodium counterions) in water, into simulations of the interface of crystalline cellulose towards water. Finally polyelectrolyte-cellulose systems were studied. Molecular dynamics simulations of diluted (_ 2:5 weight percent) aqueous solutions of two polyelectrolytes, namely sodium (carboxy methyl) cellulose (CMC) and sodium poly(acrylate) (PAA) have been performed. Water and counterions were taken into account explicitly. For CMC the substitution pattern is important. Simulations of CMC oligomers resulted in two different structures: One molecule takes a stretched conformation, while the other one takes a globule-like, collapsed state. In an additional simulation, which starts from a linear state, the second CMC molecules collapses possibly due to solute-solute hydrogen bonding. PAA is stretched during the whole simulation.On a local atomistic scale, CMC and PAA have different hydrogen-bond properties. The COO_ groups of PAA can only act as hydrogen bond acceptors, but due to the high negative charge density, there are still more water molecules assembled around PAA than around CMC. There are 0:029 bonds/amu respectively 0:019 bonds/amu to water for the two CMC oligomers, but more than twice as many for PAA: 0:083 bonds/amu. Beside intermolecular hydrogen bonding, there is a significant amount of intramolecular H-bonding for CMC, which is influenced by the COO-groups, which act as strong H-acceptor. In contrast to hydroxy- and carboxylic groups, ether oxygen are hardly involved in hydrogen bonding.The water-cellulose interface shows common features for both simulations of the 11-0 and 110 surface of cellulose I beta. We have simulated a cellulose-crystal with the 11-0 and 110 surface exposed to water. Both interfaces are stable with respect to surface reconstruction and water penetration, at least on the nanosecond time scale and in the absence of defects. Both show essentially the crystal structure of cellulose I beta, also in the adsorption patterns for water and argon. In spite of the presence of OH groups, both surfaces are non-hydrophilic and lipophilic: Water molecules are not attracted to the surface, as they are equally happy in bulk water. On the other hand, the presence of the surface perturbs the water structure sufficiently to create free volume, in which an argon can dissolve more easily than in the denser bulk water. The wider spacing of cellulose chain allows the 110 surface to expose more of the hydrophobic grooves where lipophilic adsorption takes place. In contrast, the protruding OH groups are less affected by chain packing, so the behavior towards water is similar for both surfaces. We did a direct comparison of the adsorption properties of poly(acrylate) and (carboxy methyl) cellulose on different monoclinic cellulose surfaces. Four systems have been simulated: 110-CMC, 11-0-CMC and 110-PAA and 11-0-PAA. Every systems consists of the water solvent, a cellulose-crystal and the polyelectrolyte. As found in experiment, CMC does adsorb onto the cellulose surface, and PAA does not. This is due to a high number of hydrogen bonds from the cellulose surface to the CMC-oligomers. There are hardly any hydrogen bonds between cellulose and PAA. One (carboxy methyl) cellulose is at on the surface, whereas other oligomers take a end-on-the-surface conformation. The anhydroglucose unit which is in contact with the cellulose crystal aligns parallel to the cellobiose-units of the crystal (200-plane).
Es wurden verdünnte (2.5 Gewichtsprozent) Lösungen von Polyelektrolyten ((Carboxy methyl) Zellulose und Polyacrylat) in Wasser simuliert. Wasser und Natrium-Gegenionen waren Teil des Simulationsmodells.Unsere Molekulardynamik Simulationen von CMC führen in Abhängigkeit vom Substitutionsmuster zu zwei unterschiedlichen CMC-Strukturen: Ein CMC-Oligomer behält seine gestreckte Konformation, ein zweites nimmt eine geknäulte Form an. Diese globulartige Struktur ist unabhängig von der Anfangskonformation (gestreckt oder schon geknäult). Polyacrylsäure (PAA) ist gestreckt.CMC und PAA haben verschiedene inter- und intramolekulare Wasserstoffbrückenbindungen. Die COO-Gruppe der Polyacrylsäure ist ein starker H-Akzeptor. Durch die negative Ladung ist an PAA mehr Wasser (pro Monomer, pro Masse) gebunden als an CMC. Die beiden simulierten CMC-Oligomere haben 0:029 H-Bindungen/amu (gestreckte Konformation) bzw. 0:019 H-Bindungen/amu (geknäulte). PAA hat 0:083 Bindungen/amu mit Wasser.Beide Zelluloseoberflächen (110 und 11-0) eines monoklinen Kristalls haben gemeinsame Eigenschaften. Beide Oberflächen sind gegen Wasser stabil. Es findet keine Umstrukturierung in den Simulationen mit reinem Wasser statt. Die Kristallstruktur überträgt sich auf das Adsorptionsmuster von Argon und Wasser über der Grenzschicht. Trotz der OH-Gruppen auf der Oberflächen ist Cellulose lipophil und hydrophob. Wasser wird nicht von der Oberfläche angezogen. Jedoch stört die Gegenwart des Kristalls die Wasserstruktur und es bildet sich ein freies Volumen, in dem sich Argon-Atome aufhalten. Die breiteren Lücken zwischen den Zellbioseketten der 110-Oberfläche legen dort stärker lipophilen Bereiche frei: Auf der 110 Oberfläche adsorbiert mehr Argon. Vorstehenden OH-Gruppen auf der Oberfläche haben ähnliche Eigenschaften auf beiden - der 'breiten' 110 und der 'schmalen' 11-0 - Oberfläche.Es wurden vier verschiedene Kombinationen von Oberflächen und Polyelektrolyten simuliert. Der direkte Vergleich der Adsoption von CMC und PAA auf der Zelluloseoberfläche gibt das Experiment wieder: CMC adsorbiert, PAA nicht. CMC wird durch viele Wasserstoffbrückenbindungen von der Zelluloseoberfläche, besonders von der O2 und O6 Gruppe gebunden. Zwischen PAA und Zellulose gibt es kaum H-Brücken.Die adsorbierten CMC-Oligomere stehen mit einem Ende auf der Oberfläche. Der Glucosering in Kontakt mit der Oberfläche richtet sich parallel zur 200 Kristallebene aus. Nur ein CMC-Oligomer liegt flach auf der Kristalloberfläche.Der 11-0-Zellulosekristall ist in der Gegenwart von CMC oder PAA nicht stabil. Es bildet sich ein Defekt auf der Oberfläche in der Form eines Knicks.
Subject Headings: Molekulardynamik
Simulation
Zellulose
Polyacrylsäure
Carboxymethylzellulose
Grenzflächen
URI: http://hdl.handle.net/2003/2515
http://dx.doi.org/10.17877/DE290R-14827
Issue Date: 2002-04-03
Provenance: Universität Dortmund
Appears in Collections:Physikalische Chemie

Files in This Item:
File Description SizeFormat 
biermannunt.pdfDNB13.36 MBAdobe PDFView/Open


This item is protected by original copyright



This item is protected by original copyright rightsstatements.org