Authors: Schmiedt-Kalenborn, Anke
Lingnau, Lars Andree
Manka, Matthias
Tillmann, Wolfgang
Walther, Frank
Title: Fatigue and corrosion fatigue behaviour of brazed stainless steel joints AISI 304L/BAu-4 in synthetic exhaust gas condensate
Language (ISO): en
Abstract: As brazed stainless steel components in service often have to withstand cyclic loads in corrosive environments, the corrosion fatigue properties of brazed joints have to be characterised. Application-relevant corrosion fatigue tests in corrosive media are extremely rare for brazed joints and cyclic deformation curves are barely investigated. In this study, fatigue tests of brazed AISI 304L/BAu-4 joints were performed in air and synthetic exhaust gas condensate K2.2 according to VDA 230-214. The fatigue behaviour of the brazed joints was compared to properties of the austenitic base material. Strain, electrical, magnetic, temperature and electrochemical measurement techniques were applied within fatigue and corrosion fatigue tests to characterise the cyclic deformation and damage behaviour of the brazed joints. It was found that the fatigue strength of 397 MPa at 2 × 106 cycles was reduced down to 51% due to the superimposed corrosive loading. Divergent microstructure-related damage mechanisms were identified for corrosion fatigue loadings and fatigue loadings of specimens in the as-received and pre-corroded conditions. The investigations demonstrate the important role of corrosive environments for the mechanical performance of brazed stainless steel joints.
Subject Headings: Brazed joint
AISI 304L/BAu-4
Fatigue
Corrosion fatigue
Synthetic exhaust gas condensate
Subject Headings (RSWK): Materialermüdung
Korrosion
URI: http://hdl.handle.net/2003/38013
http://dx.doi.org/10.17877/DE290R-19996
Issue Date: 2019-03-29
Rights link: https://creativecommons.org/licenses/by/4.0/
Appears in Collections:Fachgebiet Werkstoffprüftechnik

Files in This Item:
File Description SizeFormat 
materials-12-01040.pdf9.24 MBAdobe PDFView/Open


This item is protected by original copyright



All resources in the repository are protected by copyright.