Authors: Scholz, Ronja
Delp, Alexander
Walther, Frank
Title: In situ characterization of damage development in Cottonid due to quasi-static tensile loading
Language (ISO): en
Abstract: Cottonid is a layered material based 100% on cellulose that holds excellent material properties by being completely sustainable. The finite nature of petroleum-based resources nowadays makes these properties significant for technical applications again. To understand how Cottonid reacts to application-oriented mechanical loads and how it fails, development of microstructural damage on the surface and in the volume of Cottonid was studied using innovative in situ testing techniques for the first time. Quasi-static tensile tests were comparatively performed in a scanning electron microscope as well as a microfocus computer tomograph, and the development of defects present in the initial condition of the material was investigated. In the elastic region, no visible damage initiation on the surface and a decrease of overall void volume within the gauge length could be detected. When reaching the yield strength, crack initiation on the surface starts at critical areas, like pores and microcracks, which propagation and assembly could be visualized via scanning electron micrographs. In the plastic region, an increase in void volume could be shown in the gauge length until final failure of the specimen. Innovative material testing techniques presented in this study support lifetime estimation in technical applications and understanding of process–structure–property relations. Particularly, characterization of microstructural damage development due to a mechanical load, which leads to final failure of the specimen, is essential to be able to create material models for lifetime prediction in respect to variable manufacturing or application parameters.
Subject Headings: Cottonid
Cellulose
In situ testing
Scanning electron microscope
Microfocus computer tomograph
Quasi-static loading
Microstructure
Damage development
Damage mechanisms
Crack initiation
Subject Headings (RSWK): Vulkanfiber
Cellulose
In situ
Rasterelektronenmikroskop
Mikrocomputertomographie
Zugversuch
Mikrostruktur
Werkstoffschädigung
Rissbildung
URI: http://hdl.handle.net/2003/39144
http://dx.doi.org/10.17877/DE290R-21062
Issue Date: 2020-05-09
Rights link: https://creativecommons.org/licenses/by/4.0/
Appears in Collections:Fachgebiet Werkstoffprüftechnik

Files in This Item:
File Description SizeFormat 
materials-13-02180.pdf8.32 MBAdobe PDFView/Open


This item is protected by original copyright



All resources in the repository are protected by copyright.