Titel: Comparison of high-temperature compression and compression-compression fatigue behavior of magnesium alloys DieMag422 and AE42
Sprache (ISO): en
Zusammenfassung: Due to their high strength-to-weight-ratio, magnesium alloys are very attractive for use in automotive engineering. For application at elevated temperatures, the alloys must be creep-resistant. Therefore, the influence of the operating temperature on the material properties under quasistatic and cyclic load has to be understood. A previous study investigated tensile-tensile fatigue behavior of the magnesium alloys DieMag422 and AE42 at room temperature (RT). The aim of this study was the comparison of both alloys regarding compression, tensile, and compression-compression fatigue behavior. The quasistatic behavior was determined by means of tensile and compression tests, and the tensile-compression asymmetry was analyzed. In temperature increase fatigue tests (TIFT) and constant amplitude tests (CAT), the temperature influence on the cyclic creeping (ratcheting) behavior was investigated, and mechanisms-relevant test temperatures were determined. Furthermore, characteristic fracture mechanisms were evaluated with investigations of the microstructure and the fracture surfaces. The initial material was analyzed in computed tomographic scans and energy dispersive X-ray (EDX) analyses.
Schlagwörter: Magnesium
Fatigue
Compression
Rare earth
AE42
DieMag422
Tensile test
Compression test
Ratcheting
High temperature
Schlagwörter (RSWK): Magnesium
Materialermüdung
Druckversuch
Seltenerdmetall
Magnesiumlegierung
Zugversuch
Ratcheting
Hochtemperatur
URI: http://hdl.handle.net/2003/38552
http://dx.doi.org/10.17877/DE290R-20471
Erscheinungsdatum: 2020-01-21
Rechte (Link): https://creativecommons.org/licenses/by/4.0/
Enthalten in den Sammlungen:Fachgebiet Werkstoffprüftechnik

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
materials-13-00497-v2.pdf5.9 MBAdobe PDFÖffnen/Anzeigen


Diese Ressource ist urheberrechtlich geschützt.



Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.